Hss steel sheet:
specification: hot-rolled steel sheet thickness 2.5-10.5mm
width 800mm
length 1500-2000mm
cold -rolled steel sheet thickness 1.0-2.5mm
width 750mm
length 1500-2000mm
delivery condition: annealed hardness hb=255
package: suitable for export
the detailed hss material we could offer:
1. w6mo5cr4v2 (gb), it is similar to m2( astm), s6-5-2(din), skh51(jis)
chemical composition: c 0.85, si 0.38, mn 0.35, p=0.030, s=0.030, cr 4.10, w 6.00, mo 4.80 v 1.85
annealed hardness: hb=255
heat treatment temp: hardening 1210-1230 temperings 550
secondary 63-65 hrc
application: be used widely in making all kinds of knives and durable cold working molds
2. w6mo5cr4v2co5 (gb), it is similar to m35( astm), 1.3243(din), skh35(jis)
chemical composition: c 0.93, si 0.38, mn 0.35, p=0.030, s=0.030, cr 4.10, w 6.30, mo 4.80 v 1.85, co 5.00
annealed hardness: hb=269
heat treatment temp: hardening 1200-1220 temperings 550
secondary 64-67 hrc
application: steel for difficult and hi-speed cutting blades, blades which lay particular on durable
3. w2mo9cr4vco8 (gb), it is similar to m42 ( astm), 1.3247(din), skh59(jis)
chemical composition: c 1.10, si 0.55, mn 0.35, p=0.030, s=0.030, cr 4.10, w 1.50, mo 9.50 v 1.05, co 8.00
annealed hardness: hb=269
heat treatment temp: hardening 1210-1230 temperings 550
secondary 65-67 hrc
application: steel for difficult and hi-speed cutting blades, blades which lay particular on durable
4. w18cr4v (gb), it is similar to t1 ( astm), 1.3355(din), skh2(jis)
chemical composition: c 0.75, si 0.35, mn 0.35, p=0.030, s=0.030, cr 4.05, w18, v 1.10
annealed hardness: hb=255
heat treatment temp: hardening 1270-1285 temperings 560
secondary 62-65 hrc
application: steel for common cutting blades
5. w9mo3cr4v (gb)
chemical composition: c 0.83, si 0.35, mn 0.35, p=0.030, s=0.030, cr 4.05, w 8.90, mo 2.90 v 1.45
annealed hardness: hb=255
heat treatment temp: hardening 1220-1240 temperings 550
secondary 63-65 hrc
application: chinese material, similar capability to m2
6. w6mo5cr4v2 co(gb), it is equal to m2 modify ( astm)
chemical composition: c 0.80, si 0.38, mn 0.35, p=0.030, s=0.030, cr 4.10, w 5.40, mo 4.80 v 2.10, co=0.5
annealed hardness: hb=255
heat treatment temp: hardening 1210-1230 temperings 550
secondary 62-64 hrc
application: better toughness than m2
the detailed die steel material we could offer:
1. cr12mo1v1(gb), it is similar to d2( astm), 1.2379(din), skd11(jis)
chemical composition: c 1.50, si 0.35, mn 0.35, p=0.030, s=0.030, cr 12.10, w =0.40,
mo 0.85 v 0.6
annealed hardness: hb=255
heat treatment temp: hardening 1010-1050 temperings 200 550
se
Company Profile
|
Business Type: |
Hss/die steel sheet,hss/die round bar,gear hob,saw blade,side face cutter,grinder machine,band saw machine, gear wheels, gear shaft, sector gear wheels |
|
Comapany: |
Halee group limited |
|
Year of Establishment: |
2006 |
|
Address: |
Hongtang street |
|
City: |
Ningbo |
|
Zip/Postal: |
315000 |
|
State: |
China |
|
Country: |
China |
.